CYCOLAC™ EX75 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RXQyvQ_CYCOLACEX75resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Multi-purpose, extrusion ABS providing a favorable balance of engineering properties. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 40.0 | MPa | ASTM D638 |
| Fracture | 33.1 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.4 | % | ASTM D638 |
| Fracture | 43 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2410 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 73.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 420 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 94.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1160 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 93.3 | °C | |
| Suggested Max Moisture | 1.0E-3 | % | |
| Cylinder Zone 1 Temp. | 171 - 188 | °C | |
| Cylinder Zone 2 Temp. | 182 - 199 | °C | |
| Cylinder Zone 3 Temp. | 177 - 204 | °C | |
| Cylinder Zone 4 Temp. | 179 - 210 | °C | |
| Adapter Temperature | 179 - 204 | °C | |
| Melt Temperature | 199 - 218 | °C | |
| Die Temperature | 179 - 216 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 4 hrs |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| SABIC® PP RELY 61EK61PS | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PP |
| TECHNO ABS F5450 W | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Unipren® Elastomers A3 NTLA010 55A UP302 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Bergamid™ B70 G33 U GR258 | PolyOne Corporation | Nylon 6 | Bergamid™ |