CarbonResin PR 25
| Category: | Unspecified , Unspecified |
| Manufacturer: | Carbon3D, Inc. |
| Trademark: | CarbonResin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RXNO1g_CarbonResinPR25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PR 25 is a rapid production material that has excellent resolution, prints quickly, and is able to withstand moderate functional testing. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1 | 1.10 - 1.12 | g/cm³ | |
| Viscosity (25°C) | 1.60 - 1.80 | Pa·s |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 2 | 1400 - 1500 | MPa | ASTM D638 |
| -- 3 | 600 - 950 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 4 | 42.0 - 50.0 | MPa | ASTM D638 |
| Yield 5 | 26.0 - 32.0 | MPa | ASTM D638 |
| Fracture 6 | 26.0 - 32.0 | MPa | ASTM D638 |
| Fracture 7 | 42.0 - 50.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 8 | 3.0 - 5.0 | % | ASTM D638 |
| Fracture 9 | 15 - 28 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -- 10 | 2000 - 2500 | MPa | ASTM D790 |
| -- 11 | 1100 - 1300 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- 12 | 75.0 - 85.0 | MPa | ASTM D790 |
| -- 13 | 35.0 - 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 14 | 24 - 28 | J/m | ASTM D256 |
| -- 15 | 18 - 21 | J/m | ASTM D256 |
| Notched Izod Impact | ASTM D256 | ||
| -- 16 | 2.30 - 2.70 | kJ/m² | ASTM D256 |
| -- 17 | 1.70 - 2.00 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -- 18 | 380 - 420 | J/m | ASTM D4812 |
| -- 19 | 150 - 190 | J/m | ASTM D4812 |
| Unnotched Izod Impact | ASTM D256 | ||
| -- 20 | 37.0 - 41.0 | kJ/m² | ASTM D256 |
| -- 21 | 15.0 - 19.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed 22 | 52.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed 23 | 61.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 24 | 41.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 25 | 45.0 | °C | ASTM D648 |
| Glass Transition Temperature | DMA | ||
| -- 26 | 47.0 | °C | DMA |
| -- 27 | 90.0 | °C | DMA |
| CLTE - Flow | 1.3E-4 - 1.4E-4 | cm/cm/°C | ASTM E228 |
| Note Message | |
|---|---|
| 1 . | Liquid |
| 2 . | UV-Cured |
| 3 . | Green |
| 4 . | UV-Cured |
| 5 . | Green |
| 6 . | Green |
| 7 . | UV-Cured |
| 8 . | UV-Cured |
| 9 . | Green |
| 10 . | UV-Cured |
| 11 . | Green |
| 12 . | UV-Cured |
| 13 . | Green |
| 14 . | UV-Cured, Machined Notch |
| 15 . | Green, Machined Notch |
| 16 . | Green, Machined Notch |
| 17 . | UV-Cured, Machined Notch |
| 18 . | Green |
| 19 . | UV-Cured |
| 20 . | Green |
| 21 . | UV-Cured |
| 22 . | Green |
| 23 . | UV-Cured |
| 24 . | Green |
| 25 . | UV-Cured |
| 26 . | E', Green |
| 27 . | tan(d), Green |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 AR 20 TFE 10 | RTP Company | Nylon 66 | RTP |
| Spartech Polycom E66091 | Spartech Polycom | PVC, Unspecified | Spartech |
| DENITER C 3010 | Vamp Tech | PC+PBT | DENITER |
| KumhoSunny ABS HU650Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Iupilon® LGH2330M | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |