XYLEX™ X7300CL resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWIqFM_XYLEXX7300CLresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/2.16 kg | 21 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 44 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 265°C/2.16 kg | 20.0 | cm³/10min | ISO 1133 |
| 300°C/1.2 kg | 42.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1840 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 49.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 52.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture 5 | 150 | % | ASTM D638 |
| Fracture | > 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1940 | MPa | ASTM D790 |
| -- 7 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 56 | J/m | ASTM D256 |
| 23°C | 660 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| -10°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 95.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 90.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 14 | 92.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 15 |
| -- | 107 | °C | ISO 306/B50 |
| -- | 106 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 249 | °C | |
| Middle Temperature | 243 - 266 | °C | |
| Front Temperature | 249 - 271 | °C | |
| Nozzle Temperature | 249 - 271 | °C | |
| Processing (Melt) Temp | 249 - 271 | °C | |
| Mold Temperature | 43.3 - 60.0 | °C | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PE 4L1 | Witcom Engineering Plastics B.V. | PE, Unspecified | Witcom PE |
| Andur 85 APLF | Anderson Development Company | PUR-Ether/TDI | Andur |
| Innothane® IE-20AH | Innovative Polymers, Inc. | TSU-Ether | Innothane® |
| ADVANCENE™ EE-1801-BSB | ETHYDCO | LLDPE | ADVANCENE™ |
| Geon™ Vinyl Flexible HC18580 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |