REPOL® AM650N
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWHoXm_REPOL-AM650N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol AM650N is recommended for use in Injection Moulding processes. It is an ideal material to use in moulding articles with intricate long flow paths and multicavity moulding. Repol AM650N is a material of choice for use in compounds for appliance parts and automotive components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 65 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 12 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1350 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP5A20CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Network Polymers SAN 290 | Network Polymers, Inc. | SAN | Network Polymers SAN |
| LAMINEX® 2100 | Schwartz Technical Plastic | PF | LAMINEX® |
| LNP™ THERMOCOMP™ WX05505 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| OnFlex™ AF 7210-50 | PolyOne Corporation | TPE | OnFlex™ |