Tufprene™ 126S
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Tufprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RUMc4P_Tufprene-126S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrene/butadiene block copolymer with enhanced styrenic resins compatibility for heightened impact strength. Superior antiblocking property. Flexible container delivery available. It is supplied in pellet form. Styrenic resins modifier, imparting increased impact strength, mainly for food containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.5 | g/10 min | |
| 200°C/5.0 kg | 20 | g/10 min | |
| Styrene/Butadiene | 40/60 | Internal Method | |
| Viscosity - @ 25% solution in toluene 1(23°C, 2.00 mm) | 440 | mPa·s | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 23°C, 2.00 mm, Compression Molded) | 91 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain, 23°C, 2.00 mm) | 4.50 | MPa | ISO 37 |
| Tensile Stress (Yield, 23°C, 2.00 mm) | 25.0 | MPa | ISO 37 |
| Tensile Elongation (Break, 23°C, 2.00 mm) | 790 | % | ISO 37 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TP8CDB (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Andur AL 62 DP | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Durethan® BKV 30 EF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Grilamid® XE 4108 nat | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| LEXAN™ 943A resin | SABIC Innovative Plastics | PC | LEXAN™ |