TAROLOX 111 G4 DX02
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RSIyIy_TAROLOX-111-G4-DX02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET medium viscosity 20% glass fibres reinforced, flame retardant UL94 UV, heat stabilized, good flow, very good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. Designed for electrical applications requiring the compliance with the European Directive 2002/95/EC (RoHS Decree). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.60 to 0.80 | % | |
| Flow | 0.20 to 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Granule Humidity 1 | < 0.030 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(850°C) | 20 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 8200 | MPa | ISO 178 |
| Flexural Stress 4 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 236 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.750 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 100 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 25 RS 5 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Yuyao PP PP Weathering | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Durethan® BF 4222 00000 | LANXESS GmbH | PBT | Durethan® |
| Flontech® FT-BRR55-M5-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Sylvin 83027-65FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |