Bio-Polymer (PLA, PHB, ...). Unfilled. Good elongation. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.20 to 0.60 | % | |
| Flow : 2.00 mm | 0.25 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.2 | % | |
| Break, 23°C | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 50.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 55.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 to 50.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 170 to 190 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 H AR 5 TFE 10 | RTP Company | Nylon 66 | RTP |
| Ultraform® N 2320 003 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| DSR TL-103 | Dragon Special Resin (Xiamen) Co., Ltd. | PET | DSR |
| Generic ABS+Acrylic | Generic | ABS+Acrylic | Generic |
| Hostaform® C 9021 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |