Kingfa PBT JE2-R2
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RRFCi0_Kingfa-PBT-JE2-R2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT JE2-R2 is an acrylonitrile butadiene styrene PBT (ABS PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT JE2-R2 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.50 - 0.60 | % | ASTM D955 |
| Transverse flow : 23°C | 0.60 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 2100 | MPa | ASTM D790 |
| Flexural Strength 4 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 220 - 230 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 250°CInjection Speed: 60 to 80% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP LPP20BC77BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| GPPC SAN D-12 | GPPC Chemical Co., Ltd. | SAN | GPPC |
| Enviramid® N1315HL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| Petrotene® PP A3 T40 NTLA010 PH320 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Sumitomo Phenolic GF 8202 L24 | SBHPP | Phenolic | Sumitomo Phenolic |