TECHNYL® 1021GF6 BRIGHT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RQWgO3_TECHNYL-1021GF6-BRIGHT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL 1021GF6 BRIGHT is a polyamide 6, 30% glass fiber reinforced, for injection molding. This product is available in bright color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.65 | -- | % | |
| Flow | 0.35 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 175 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | -- | % | ASTM D638 |
| Flexural Modulus | 8900 | -- | MPa | ASTM D790 |
| Flexural Strength | 260 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 130 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | -- | °C | ASTM D648 |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 3.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANBLEND FS8 ASUV4 | Polykemi AB | ASA+PC | SCANBLEND |
| Sup-tech A101 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| Durethan® AKV 35 CX H2.0 900876 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |
| Hostaform® C 13021 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Deprene 201-87 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |