Stat-Tech™ AT-CB2/000 CR
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RPOrN3_Stat-Tech-AT-CB2-000-CR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stat-Tech™ AT-CB2/000 CR XP020229R2 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 to 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.5 to 2.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2070 to 4140 | MPa | ASTM D638 |
| Tensile Strength (Break) | 51.7 to 68.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 to 20 | % | ASTM D638 |
| Flexural Modulus | 1380 to 3450 | MPa | ASTM D790 |
| Flexural Strength | 82.7 to 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 53 to 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 153 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 to 1.0E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 75.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1843 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Wellamid® GF1750-N1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Fainplast PVC KL 0209 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HiFill® PA6/6 GF/M35 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Pearlthane® ECO D12T80 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® ECO |