Chemiton TGB2NA 30
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Franplast S.r.l. |
| Trademark: | Chemiton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RO4giz_Chemiton-TGB2NA-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEBS based compound. Ideal for of non-toxic items, such as fashion accessories and gadgets. Very good surface finish. Application:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 90 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 5.50 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 740 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 15 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -30 to 70 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 0.0 | hr | |
| Rear Temperature | 185 to 205 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 195 to 215 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 726QE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Ultramid® 8350 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| APEX® 77-W002-F | Teknor Apex Company | PVC, Flexible | APEX® |
| ExxonMobil™ PP9574E6 | ExxonMobil Chemical | PP Random Copolymer | ExxonMobil™ |
| I. Stern SH432HG | I. STERN & CO. INC. | PS (HIPS) | I. Stern |