Staramide AG6ST43
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RNGrD9_Staramide-AG6ST43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide AG6ST43 is an Impact Modified, Glass Fiber Reinforced Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.50 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2 | ISO 180/1A | ||
| -40°C | 16 | kJ/m² | |
| -20°C | 18 | kJ/m² | |
| 23°C | 22 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 245 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 225 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 250 | °C | ISO 306/B120 |
| CLTE - Flow (23 to 80°C) | 4.0E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 80*10*4 |
| 3 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 T20 NTLA010 NR425 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Formolon® 622R | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Dynaprene® SE9050A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| ELASTOSIL® LR 3003/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Lotader® TX 8030 | Arkema | EEA | Lotader® |