Braskem PE GM5010T2
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RLbCpd_Braskem-PE-GM5010T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The GM 5010 T2 is a High Density Polyethylene compounding with high molar mass, specially developed for the manufacturing of extruded pipes. This resin is produced with bimodal technology, it has excellent mechanical properties, besides excellent resistance to stress cracking. This resin has MRS (Minimum Required Strength) of 8 MPa according to ISO 9080, and is classified as PE 80 according to ISO 12162. GM 5010 T2 contains carbon black pigment that guarantees resistance against photodegradation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.45 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Carbon Black Content | 2.0 to 2.5 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 23.0 | MPa | |
| Break, Compression Molded | 34.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 9.1 | % | |
| Break, Compression Molded | 800 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1090 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 70.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIREX HP8250 | Formosa Plastics Corporation | PS (HIPS) | TAIRIREX |
| DOW™ LLDPE 6500R | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Novodur® HH-112 | Styrolution | ABS | Novodur® |
| 4TECH® 9S33500 H | 4Plas | Polyphenylene, Unspecified | 4TECH® |
| Bergamid™ AB700 UF BK138 | PolyOne Corporation | Nylon 66/6 | Bergamid™ |