CYCOLOY™ CY6310 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RLCvMR_CYCOLOYCY6310resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/2.16 kg | 16 | g/10 min | ASTM D1238 |
| 260°C/2.16 kg | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 19.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 50.0 | MPa | ASTM D638 |
| Fracture | 51.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.2 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2/50 |
| Fracture 5 | > 50 | % | ASTM D638 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2700 | MPa | ASTM D790 |
| -- 7 | 2650 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 14 14 | kJ/m² | ISO 179/1eA |
| 23°C | 55 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break No Break | ISO 179/1eU | |
| 23°C | No Break No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 600 | J/m | ASTM D256 |
| -30°C 11 | 13 13 | kJ/m² | ISO 180/1A |
| 23°C 12 | 50 50 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break No Break | ISO 180/1U | |
| 23°C | No Break No Break | ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 65.0 | J | ASTM D3763 |
| -- | 105 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 90.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 111 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | IEC 60695-10-2 | |
| 95°C 16 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI | 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | UL 94 | |
| 0.750 mm, Testing by SABIC | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 1.50 mm, Testing by SABIC | V-0 | UL 94 | |
| 2.30 mm | 5VB | UL 94 | |
| 2.30 mm, Testing by SABIC | 5VB | UL 94 | |
| 2.90 mm | 5VA | UL 94 | |
| 2.90 mm, Testing by SABIC | 5VA | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 230 - 270 | °C | |
| Front Temperature | 240 - 280 | °C | |
| Nozzle Temperature | 230 - 270 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| 16 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPF401NHT | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Sinpolene MBB3134 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Vydyne® 47H BK03 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Lupol® GP2200 | LG Chem Ltd. | PP, Unspecified | Lupol® |
| omay® US42 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC/ABS | omay® |