ENPRENE 9840
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | En Chuan Chemical Industries Co,. Ltd. |
| Trademark: | ENPRENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RLBWpD_ENPRENE-9840.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENPRENE 9840 is a styrene-butadiene-styrene block copolymer (SBS) product,. It is available in the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 26 | g/10 min | ASTM D1238 |
| Oil Type (Unspecified Oil) | 35.0 | phr | |
| Styrene/Butadiene | Ratio: 48/52 | ASTM D1416 | |
| Ash Content | 0.2 | wt% | ASTM D1416 |
| Volatile Matter | 0.50 | wt% | ASTM D1416 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 2.94 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 10.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 700 | % | ASTM D412 |
| Tear Strength | 49.0 | kN/m | ASTM D624 |
| Additional Information |
|---|
| It's effectively to offer clear SBS from 10A ~ 80A . Due to higher melt flow index and excellent processibility , direct injection is easily for various mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Amilan® CM1041LO | Toray Resin Company | Nylon 6 | Amilan® |
| Gallonprene® GP310-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GAPEX® RPP10EU60AL | Ferro Corporation | PP, Unspecified | GAPEX® |
| Elastamax™ HTE 3050 | PolyOne Corporation | PVC+NBR | Elastamax™ |
| Plaslube® ABS 8005 | Techmer Engineered Solutions | ABS | Plaslube® |