SABIC® PP 524P
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RIbEIn_SABIC-PP-524P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®PP 524P is particularly developed for (biaxially) oriented PP film extrusion with a very specific molecular structure providing the ultimate properties required for the stretching process. SABIC® PP 524P is typically used in mono layer or coextruded (B)OPP film. SABIC® PP 524P is known for its excellent metallisation behaviour. SABIC® PP 524P is a low mfi material typically used in extrusion applications like sheet and thermoforming. SABIC® PP 524P is typically used in dairy, flower pots, yellow fats and disposables plates and cups. However, customers use this grade also in combination with fillers like Talc and CaCO3. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1500 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 36.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 10 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256A |
| 23°C | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 88.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 22L-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| INSTRUC PA66GF10 | Infinity LTL Engineered Compounds | Nylon 66 | INSTRUC |
| Lion Idemitsu Composites PPS G531F2 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| POLYfill PPC B8075 | Polykemi AB | PP Copolymer | POLYfill |
| Paryls® PSU F3150GL20 | Youju New Materials Co., Ltd. | PSU | Paryls® |