| 33% Glass Reinforced, Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (24 hr) | 0.91 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8800 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 148 | 112 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.6 | 6.6 | % | ISO 527-2 |
| Flexural Modulus | 7600 | -- | MPa | ISO 178 |
| Flexural Stress | 214 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 18 | -- | kJ/m² | |
| -30°C | 18 | 17 | kJ/m² | |
| 23°C | 20 | 27 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 110 | 97 | kJ/m² | |
| 23°C | 97 | 96 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | -- | kJ/m² | |
| -30°C | 17 | 16 | kJ/m² | |
| 23°C | 21 | 26 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.750 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 25.3 | -- | µgC/g | VDA 277 |
| Odor | 3 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SKYBOND® 2595 | Industrial Summit Technology Co. | API | SKYBOND® |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Andur 8-5 APLS | Anderson Development Company | PUR-Ester/TDI | Andur |
| CERTENE™ LDF-322C | Muehlstein | LDPE | CERTENE™ |
| Chansieh Phenolic J-361-2 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |