Boltaron 4205
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RHBFL4_Boltaron-4205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Boltaron 4205 is a proprietary, high heat distortion, fire retardant, extruded thermoplastic sheet designed to meet stringent FAA flammability requirements and higher in-service temperature applications. Boltaron 4205 offers excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Colors: Custom Gauges: .028 to .250 Widths: Up to 60" Lengths: Up to 120" Custom Sizes: Upon request Textures: Coarse Matte (CM) Felt (FT) Haircell (HC) Levant (LT) Mesa (MS) Suede (SD) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 49.6 | MPa | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 82.2 to 85.0 | °C | |
| 1.8 MPa, Annealed | 93.3 to 96.1 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 1 | 12.0 60.0 | sec | FAR 25.853 |
| Forming Temperature | 193 to 216 | °C |
| Note Message | |
|---|---|
| 1 . | Pass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFT1675-N1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Dynaflex™ G6713C | PolyOne Corporation | TPE | Dynaflex™ |
| Generic Nylon 66 - Glass Fabric | Generic | Nylon 66 | Generic |
| Generic PBT+ASA - Glass Fiber | Generic | PBT+ASA | Generic |
| Osterlene® PPC-20-2.0-A | Osterman & Company | PP Impact Copolymer | Osterlene® |