TECHNYL STAR™ S 60G1 V30 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RGfqnm_TECHNYL-STAR-S-60G1-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR™ S 60G1 V30 Natural is a reinforced 30% GF organophosphorous flame retarded grade based on a patented high flow polyamide 6 resin (TechnylStar). This product is heat stabilized and provides optimized injection moulding performance. This produc |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.570 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11800 | 8500 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 155 | -- | MPa | ASTM D638 |
| Break | 147 | 97.0 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.5 | -- | % | ASTM D638 |
| Break | 2.4 | 5.1 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 10500 | -- | MPa | ASTM D790 |
| -- | 10700 | 7100 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 240 | -- | MPa | ASTM D790 |
| -- | 243 | 175 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.6 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 10 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 54 | 63 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.1E+14 | -- | ohms | IEC 60093 |
| Electric Strength | 25 | 23 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 2.90 | 4.35 | IEC 60250 | |
| Dissipation Factor | -- | 0.080 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | V-0 | -- | ||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.60 mm | 800 | -- | °C | |
| Oxygen Index | 35 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 801 UV | RTP Company | Acetal (POM) Copolymer | RTP |
| RheTech Polypropylene GC10P200-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Terlux® 2802 | INEOS Styrolution Group GmbH | MABS | Terlux® |
| Ultramid® A3WG3 | BASF Corporation | Nylon 66 | Ultramid® |
| HAIPLEN EP50 T2 X2 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |