Order Products : sales@su-jiao.com
DURACON® VW-09
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURACON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RGa5r2_DURACON-VW-09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Sliding |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.50 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2 |
| Tensile Stress | 58.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Coefficient of friction- Dynamic | JIS K7218 | ||
| -- 1 | 0.280 | JIS K7218 | |
| -- 2 | 0.160 | JIS K7218 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Number | CF2001 | ||
| Specific Wear | JIS K7218 | ||
| -- 3 | 10^-3 mm³/N·km | JIS K7218 | |
| -- 4 | 70.0 | 10^-3 mm³/N·km | JIS K7218 |
| -- 5 | 5.00 | 10^-3 mm³/N·km | JIS K7218 |
| -- 6 | 0.120 | 10^-3 mm³/N·km | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.9 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.3E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.3E-4 | cm/cm/°C | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 98.0 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Injection Speed: 5-50mm/s (0.3-3m/min)Molding Cycle: Injection Holding Pressure: Gate sealing time + alpha Cooling: Plasticizing time or ejection capable time |
| Note Message | |
|---|---|
| 1 . | vs M90-44, pressure0.06MPa, 15cm/s |
| 2 . | vs C-Steel, pressure 0.98MPa, 30cm/s |
| 3 . | vs C-Steel, steel side, pressure 0.98MPa, 30cm/s |
| 4 . | vs M90-44, material side, pressure 0.06MPa, 15cm/s |
| 5 . | vs M90-44, M90-44 side, pressure 0.06MPa, 15cm/s |
| 6 . | vs C-Steel, material side, pressure 0.98MPa, 30cm/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rely-imide 600 | Henkel Ablestik | TP, Unspecified | Rely-imide |
| Ad-Tech Epoxy EL-315-IHL-2 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Cheng Yu ML3415 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| EPLAMID 66 GFS 40 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Jamplast JPTPUET | Jamplast, Inc. | TPU-Polyether | Jamplast |