MAJORIS DW401HB - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RFN2Ra_MAJORIS-DW401HB---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DW401HB - 8229 is a 40% glass fibre/bead reinforced polypropylene chemically coupled compound intended for injection moulding. The product is available in both natural (DW401HB) and black (DW401HB - 8229) but other colours can be provided on request. DW401HB - 8229 has been developed especially for the automotive applications and electrical components. APPLICATIONS Products requiring good long term heat resistance, high heat distortion temperature, rigidity, low shrinkage and high dimensional stability be made from DW401HB - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.20 - 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 53.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus 1 | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 129 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TS271A1 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| SureSpec IP-350NA | Genesis Polymers | PP Impact Copolymer | SureSpec |
| EPO-TEK® 353ND-T4 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina BLUE COLOR CONCENTRATE 06/174-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ OCP34E compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |