Hanwha Total PP FH22
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RCuvXc_Hanwha-Total-PP-FH22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FH22 is a highly rigid, high-gloss, and flame retardant polypropylene compound, using a variety of base PPs, such as HIPP (High Isotactic Polypropylene), which are manufactured with SAMSUGN TOTAL`s special processing technology to offer top-of-the-line quality. This product features superior rigidity, heat and scratch resistance and low blooming. In addition to high flowability, FH22 features outstanding processability, flame-retardancy and add to the appearance of the finished product. FH22 is widely used in the exterior parts of electric and electronic products requiring high flame retardant property. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.4 - 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 37.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 1860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 39.2 - 78.5 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa |
| Injection instructions |
|---|
| Injection Speed: 50 to 80 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hifax DRL 781P | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ STAT-KON™ DEL33EC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 7833-70C Grey 9613 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| StarPrene® 6101-70 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPrene® |
| LEXAN™ LUX7630C resin | SABIC Innovative Plastics | PC | LEXAN™ |