OPTAMID® PA 6 G Datasheet,Nylon 6,Schwartz Technical Plastic-SHANGHAI SUSHENG

Message
Applications: Deflection rope sheaves for elevators

General Information
Uses	Machine/mechanical parts
Forms	Particle
Processing Method	Casting

Physical	Dry	Conditioned	Unit	Test Method
Density	1.15	--	g/cm³	ISO 1183
Water Absorption				ISO 62
23°C, 24 hr	2.2	--	%	ISO 62
Saturated, 23°C	7.0	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	150	120	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	3500	2700	MPa	ISO 527-2
Tensile Stress				ISO 527-2
Yield	80.0	60.0	MPa	ISO 527-2
Fracture	130	55.0	MPa	ISO 527-2
Tensile Strain (Break)	> 25	--	%	ISO 527-2
Flexural Modulus	3100	2400	MPa	ISO 178
Coefficient of Friction				ASTM D1894
With steel-dynamic	0.040	0.080		ASTM D1894
With steel-static	0.35	0.42		ASTM D1894

Impact	Dry	Conditioned	Unit	Test Method
Notched Izod Impact	> 3.7	> 15	kJ/m²	ISO 180
Unnotched Izod Impact Strength	No Break	No Break		ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	210	--	°C	ISO 75-2/B
1.8 MPa, not annealed	120	--	°C	ISO 75-2/A
Melting Temperature (DSC)	220	--	°C	ISO 3146
CLTE - Flow (20 to 100°C)	7.0E-5 - 8.0E-5	--	cm/cm/°C	ISO 11359-2
Specific Heat	1670	--	J/kg/°C	ASTM C351
Thermal Conductivity	0.25	--	W/m/K	ISO 8302

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+12	1.0E+10	ohms	IEC 60093
Dielectric Strength	50	20	kV/mm	IEC 60243-1
Dielectric Constant	3.70	--		IEC 60250
Dissipation Factor	0.030	--		IEC 60250

Additional Information
干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >20 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >22 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40°C
调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >11 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >15 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: 120°CTensile Strain at Break, ISO 527-1-2: > 25%Notched Izod Impact, ISO 180: >15 kJ/m²

Additional Information

干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >20 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >22 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40°C

调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >11 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >15 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: 120°CTensile Strain at Break, ISO 527-1-2: > 25%Notched Izod Impact, ISO 180: >15 kJ/m²

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Schwartz Technical Plastic
Trademark:	OPTAMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RBkYa4_OPTAMID-PA-6-G.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC 6926 AF 017	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RTP 102 Z	RTP Company	PP, Unspecified	RTP
Bergamid™ B65 G30 black IG	PolyOne Corporation	Nylon 6	Bergamid™
Sylvin 9604-90 Grey 9602	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LEXAN™ HFD4412 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™