Order Products : sales@su-jiao.com
AFFINITY™ HT1285G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RBg5hM_AFFINITYHT1285G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* HT1285G Polyolefin Plastomer (POP) is specifically designed as a high performance sealant for demanding packaging applications. AFFINITY HT 1285G provides high packaging integrity through improved hot tack strength, enhanced caulkability, superior seal though contamination, and low temperature seal initiation. It helps enable hermetic packaging on today's high speed packaging lines or with demanding substrates, and supports reducing sealant failure and potential related food waste. AFFINITY HT 1285G has been developed for processing on Cast, Blown, and Extrusion Coating film production lines.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 5.80 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 5.30 | MPa | ASTM D882 |
| MD : Break, 25 µm | 48.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 470 | % | ASTM D882 |
| TD : Break, 25 µm | 720 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 290 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25 µm | 78 | g | ASTM D1922 |
| TD : 25 µm | 410 | g | ASTM D1922 |
| Seal Initiation Temperature | 88.0 | °C | ASTM D1525 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 96.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (25.0 µm, Cast Film) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA6 A1G6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| Tecotek® PC40 NL VB02 | Eurotec Engineering Plastics | PC+PBT | Tecotek® |
| Alcryn® 2060 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| Laprene® 8K1000A90 | SO.F.TER. SPA | SEBS | Laprene® |
| LNP™ LUBRICOMP™ RCL36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |