Generic PUR-Ester/TDI
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RAK7Ng_Generic-PUR-Ester-TDI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PUR-Ester/TDI This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 - 1.26 | g/cm³ | ASTM D792 |
| -- | 1.21 - 1.27 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow (23°C) | 1.1 - 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 50 - 97 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 44.8 - 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 280 - 710 | % | ASTM D638 |
| Compressive Strength (23°C) | 0.621 - 14.2 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain, 23°C | 1.51 - 12.2 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.55 - 18.5 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Yield, 23°C | 49.5 - 59.5 | MPa | ASTM D412 |
| Fracture, 23°C | 37.8 - 54.0 | MPa | ASTM D412 |
| 23°C | 48.1 - 50.7 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 390 - 730 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 40.3 - 134 | kN/m | ASTM D624 |
| Cracking | 17 | kN/m | ASTM D470 |
| Compression Set | 1.0 - 38 | % | ASTM D395 |
| Bayshore Resilience | 27 - 40 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 1.0 - 13 | min | |
| Thermoset Mix Viscosity | 380 - 3250 | cP | ASTM D2393 |
| Demold Time | 20 - 1400 | min | |
| Post Cure Time | 6.0 - 78 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PUR-Ester/TDIThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF30 HY | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Karina BLUE PVC COMPOUND 900D06/469-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 GF/M40 ML2 GY | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Sylvin 9067F3 Red 6252 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8707-84 White 1564 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |