Jamplast JPSANGI
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R9GbGC_Jamplast-JPSANGI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jamplast SAN resin is a general purpose SAN copolymer that offers an excellent balance of chemical resistance, physical properties, practical toughness, and processability for injection molded or extruded applications. This resin has undergone biocompatibility testing in accordance with USP XXIII Class VI guidelines. Applications include houseware, appliance, water filter housing and medical. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 3470 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 71.7 | MPa | |
| Break, 3.18 mm | 71.7 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 2.5 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 3870 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.18 mm) | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 96.7 | °C | |
| 0.45 MPa, Annealed, 3.18 mm | 102 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 85.6 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 98.3 | °C | |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 19 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.60 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 204 | °C | |
| Middle Temperature | 218 | °C | |
| Front Temperature | 232 | °C | |
| Nozzle Temperature | 227 | °C | |
| Processing (Melt) Temp | 199 to 232 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® R200MK | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| STRATOR® A-5 | EPIC Polymers | Nylon 66 | Strator® |
| VALOX™ VC108 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| Loyblend® HA-1500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS+Acrylic | Loyblend® |
| Sylvin 6235-80UV Grey 9591 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |