MFE® -36

Category:	Vinyl Ester , Vinyl Ester
Manufacturer:	Huachang Polymer Co., Ltd.
Trademark:	MFE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	R8YWd5_MFE--36.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MFE-36 is based on bisphenol-A epoxy vinyl ester resin, modified by methacrylic acid. It has excellent flexibility.

PROPERTY

Excellent process performance and wet-out with fibers.

Excellent corrosion-resistance, especially to inorganic acid, alkali, salt, etc.

Excellent mechanical properties.

High tensile elongation.

Low peak exotherm, low shrinkage.

APPLICATION

Can be used in various processes, such as hand lay-up, pultrusion, spray-up, filament winding, etc

Various FRP products.

Corrosion resistant flooring, sealing material, FRP layer on the surface of metal and concrete structure.

General Information
Features	Acid Resistant Alkali Resistant Good Corrosion Resistance Good Flexibility High Elongation Low Exotherm Low Shrinkage Rapid Wetting Salt Water/Spray Resistant
Uses	Flooring Maintenance/Repair Protective Coatings Sealants
Appearance	Yellow
Processing Method	Filament Winding Hand Lay-up Pultrusion Spraying

Physical	Nominal Value	Unit	Test Method
Acid Value	7.00 to 13.00	mg KOH/g
Solids Content	51 to 59	%

Thermal	Nominal Value	Unit	Test Method
Thermal Stability (80°C)	> 1	day

Thermoset	Nominal Value	Unit
Gel Time (25°C)	15.0 to 25.0	min

Fill Analysis	Nominal Value	Unit
Brookfield Viscosity ¹(25°C)	400 to 600	mPa·s

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	40		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3400	MPa	ASTM D638
Tensile Strength	85.0	MPa	ASTM D638
Tensile Elongation (Break)	7.0	%	ASTM D638
Flexural Modulus	3200	MPa	ASTM D790
Flexural Strength	150	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	105	°C	ASTM D648

Note Message
1 .	Brookfield #63@60rpm

Resin Grade	Manufacturer	Category	Trademark
MARPOL® PSH 6073	Marco Polo International, Inc.	PS (HIPS)	MARPOL® PSH
NILENE® P10 K30T	Taro Plast S.p.A.	PP Homopolymer	NILENE®
Chemical Resources PMMA1100	Chemical Resources, Inc.	Acrylic (PMMA)	Chemical Resources
Karina BLACK PVC COMPOUND CAK 65-48/1-F	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
MACOMASS PP MM-PP HI 22	MACOMASS Verkaufs AG	PP Homopolymer	MACOMASS PP