ACCUTECH™ CP0436W20L1
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R8618c_ACCUTECH-CP0436W20L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0436W20L1 is a polypropylene copolymer (PP Copoly) product, which contains a filler of 20% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 59 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 21.0 | MPa | ASTM D638 |
| Fracture | 15.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 32 | % | ASTM D638 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Flexural Strength | 25.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 102 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 56.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-2100-90 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Clariant Nylon 6/6 PA-133G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Elastron® G G400.A60.T | Elastron USA, Inc. | SEBS | Elastron® G |
| Huafon JF-P-2922 / JF-I-2918 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Hostacom M2 T02 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |