4TECH® 9KF23500 HI
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R7CzX0_4TECH-9KF23500-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9KF23500 HI is a Standard Flow Halogen Free FR-V0 Heat Stabilised, Impact Modified PBT / Polycarbonate Blend |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 60 | g/10 min | ISO 1133 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Moisture Content | < 1000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/B |
| Melting Temperature | 220 - 230 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 50.0 - 110 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 300 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7510 GF 10 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Multi-Flex® TPO D5308 X | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Nylene® 405 HS | Custom Resins Group | Nylon 6 | Nylene® |
| Huafon JF-HSY-ADP1 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Teldene® R40MLT | National Petrochemical Industries Company (NATPET) | PP Random Copolymer | Teldene® |