KRYSTALFLEX™ PE393
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | KRYSTALFLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R7CGMq_KRYSTALFLEX-PE393.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRYSTALFLEX PE393 is a high performance aliphatic polyether film intended for processing by lamination into a range of glass/plastics components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 74 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 2.76 | MPa | ASTM D412 |
| 300% strain | 5.52 | MPa | ASTM D412 |
| Tensile Strength 2(Yield) | 20.7 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 600 | % | ASTM D412 |
| Tear Strength | 52.5 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -42.2 | °C | DSC |
| Additional Information |
|---|
| Softening Range, TMA: 185 to 250°FTypical Laminating Parameters:Ultimate Temperature: 194 to 248°FUltimate Pressure: 116 to 174 psiSoaking Time: 30 min/0.25 in |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 MT6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Active Flow LP1040T | SCG Chemicals Co., Ltd. | PE Homopolymer | Active Flow |
| EPT 4045 | Mitsui Chemicals, Inc. | EPDM | EPT |
| MAJORIS FN080 | AD majoris | PP Copolymer | MAJORIS |
| Hifax TYC 1229P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |