Loyblend® TK-1000
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Loyblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R6ocek_Loyblend-TK-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Loyblend® TK-1000 is an impact modified alloy of Polycarbonate and Polyethylene terephalate polymer. This grade offers impact resistance, good dimensional stability and high heat resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 710 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 104 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 565A2R30016 Natural, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Multiuse Leostomer® LE-3170N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| 4MID® 9B22125 | 4Plas | Nylon 6 | 4MID® |
| Garathane™ X 94-350-B NAT UV-DG2 | AlphaGary | PUR-Ether | Garathane™ |
| Escorene™ Ultra FL 00112 | ExxonMobil Chemical | EVA | Escorene™ Ultra |