LNP™ THERMOCOMP™ MC004 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R5tibt_LNP-THERMOCOMP-MC004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MC004 is a compound based on Polypropylene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound MC-1004 Product reorder name: MC004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.050 to 0.25 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 48.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7300 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 32.0 | MPa | |
| -- 5 | 64.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 129 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Break |
| 5 . | Yield |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3571EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| BESTPOLUX PCAHC/02 | Triesa Plastics | PC+ABS | BESTPOLUX |
| Kemcor LDX 438 | Qenos Pty Ltd | LLDPE | Kemcor |
| Karina GREEN PVC COMPOUND 602D40/ 93-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Adflex 7635 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |