TAROLOX 2050 W G6
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R5UokE_TAROLOX-2050-W-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/PET alloy 30% glass fibres reinforced, very good surface appearance, high temperature and chemical resistance. High dimensional stability with low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 - 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.50 - 0.80 | % | Internal method |
| Flow direction | 0.30 - 0.50 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 8200 | MPa | ISO 178 |
| Flexural Stress 4 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 60 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Continuous Use Temperature 6 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | 216 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 235 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm) | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.60 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 19 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 90.0 - 130 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 130 to 150°CPre-heat Time: 2 to 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 GB 20 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| REPOL® SRM250NC | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| SUPREME Specialty PS SP8001 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| ISORENE™ A4-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| LEXAN™ OQ4005 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |