Bakelite® PF 31
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R5BwfZ_Bakelite-PF-31.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, mainly organically filled, standard moulding compound for normal stress, UL listed moulding compound 1.5 mm / V-1 (ALL), 3.0 mm / V-0 (ALL), standardized moulding compound Application Areas Mouldings of all kinds from screw caps to large casings, electrical installation material, handle casings (bars), pan handles, operating elements, toaster parts and pistons for braking power energizers, carbon brush holders, lamp casing parts, decor items, ashtrays |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.42 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.45 | % | |
| -- 2 | 0.85 | % | |
| Water Absorption - 24h/23C | 65.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 3 | 0.55 | % | |
| -- 4 | 0.45 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 300 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress | 50.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Flexural Stress 5 | 95.0 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 120 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength 6(1.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 11.0 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.30 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, All | V-1 | ||
| 3.00 mm, All | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Compression |
| 2 . | Injection |
| 3 . | Injection |
| 4 . | Compression |
| 5 . | 2.0 mm/min |
| 6 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1120E | Teknor Apex Company | TPE | Telcar® |
| TOTAL Polypropylene PPH 3866 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| XANTAR® MX 1004 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Neopor® 2200 | BASF Corporation | PS (EPS) | Neopor® |
| HiFill FR® PA4/6 GF30 FR HS X | Techmer Engineered Solutions | Nylon 46 | HiFill FR® |