TPX® MX002
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R4Nlyx_TPX-MX002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TPX® MX002 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for blow molding, extrusion, fiber (spinning) extrusion, film extrusion, or injection molding. Important attributes of TPX® MX002 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 21 | g/10 min | ASTM D1238 |
| Spiral Flow 1 | 56.0 | cm | Internal Method |
| Molding Shrinkage 2 | Internal Method | ||
| Flow | 1.5 | % | |
| Across Flow | 1.1 | % | |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 42 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 890 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 21.0 | MPa | |
| Break, 23°C | 10.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 660 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 27.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 28 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 130 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 153 | °C | ASTM D1525 |
| Melting Temperature | 224 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 65 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 2.1 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Mold Temperature: 73°C, Melt Temperature: 310 to 320°C |
| 2 . | temperature range: 260 to 280°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 7520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| WPP TPO TPO-2563 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Braskem PP C765-15NA | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| Sylvin 4200-75UV Clear Black 2108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 1100F resin | SABIC Innovative Plastics | PEI | ULTEM™ |