Honeywell PCTFE P10000HS
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | Honeywell PCTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R2RKag_Honeywell-PCTFE-P10000HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Honeywell PCTFE P-Series HS film is a copolymer poly-chlor-tri-fluoroethylene film. Honeywell PCTFE HS film has the ability to heat seal to itself utilizing impulse sealing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.08 | g/cm³ | ASTM D792 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 1030 | MPa | ASTM D882 |
| TD | 1030 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 36.2 | MPa | ASTM D882 |
| TD : Fracture | 32.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 240 | % | ASTM D882 |
| TD : Fracture | 240 | % | ASTM D882 |
| Water Vapor Transmission | 0.047 | g/m²/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 190 | °C | ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 100 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 1329 in²/lbTensile Strength @ Break, ASTM D 882, MD: 4500 to 6000 psiTensile Strength @ Break, ASTM D 882, TD: 4000 to 5500 psiElongation @ Break, ASTM 882, MD: 200 to 275%Elongation @ Break, ASTM 882, TD: 200 to 275%Secant Modulus, ASTM D 882, MD: 125000 to 175000 psiSecant Modulus, ASTM D 882, TD: 125000 to 175000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 425 g/milGraves Tear (initial), ASTM D 1004, TD: 325 to 425 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <2% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <2% shrinkageFlammability: Non-flammable |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 8260 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Daplen™ EE209AE | Borealis AG | PP, Unspecified | Daplen™ |
| Kemcor HDX 954 | Qenos Pty Ltd | HDPE Copolymer | Kemcor |
| ICORENE® 1901 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |
| Sylvin 4235-83 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |