Eltex® PF6212KE

Category:	mLLDPE , Metallocene Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	R2GZCl_EltexPF6212KE.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® PF6212KE is a metallocene LLDPE grade produced in Europe

Benefits & Features
Eltex® PF6212KE is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:

Extremely high impact strength

Excellent optical properties

Very good bubble stability and extrudability, even at low gauge and narrow die gap

Low temperature sealing characteristics

Eltex® PF6212KE is formulated with antioxidants, slip and antiblock additives and a processing aid. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance.

Applications
Eltex® PF6212KE has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required. Eltex® PF6212KE offers easy extrudability.

General Information
Additive	Processing aid Erucamide Lubricating Additive (1000 ppm) Anti-caking agent (300 ppm) 2 Antioxidation
Features	Ultra-high impact resistance Low density Low temperature heat sealability Copolymer smoothness Optical hexene comonomer Anti-caking property Antioxidation Workability, good Compliance of Food Exposure
Uses	Films Food packaging
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Film extrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.920	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	< 0.25		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Modulus			ISO 1184
1% secant, MD : 25 µm, blown film	180	MPa	ISO 1184
1% secant, TD : 25 µm, blown film	200	MPa	ISO 1184
Tensile Stress			ISO 1184
MD : Yield, 25 µm, blown film	9.00	MPa	ISO 1184
TD : Yield, 25 µm, blown film	10.0	MPa	ISO 1184
MD : Broken, 25 µm, blown film	65.0	MPa	ISO 1184
TD : Broken, 25 µm, blown film	60.0	MPa	ISO 1184
Tensile Elongation			ISO 1184
MD : Broken, 25 µm, blown film	550	%	ISO 1184
TD : Broken, 25 µm, blown film	670	%	ISO 1184
Dart Drop Impact (25 µm, Blown Film)	> 1000	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	200	g	ASTM D1922
TD : 25 µm, blown film	440	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature ¹	105 - 118	°C	ASTM D3418

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	62		ASTM D2457
Haze (25.0 µm, Blown Film)	8.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	190 - 230	°C

Note Message
1 .	2nd heating

Resin Grade	Manufacturer	Category	Trademark
DOW™ LDPE 132G	The Dow Chemical Company	LDPE	DOW™ LDPE
Delrin® 100STE NC010	DuPont Performance Polymers	Acetal (POM) Homopolymer	Delrin®
Gallonprene® GP210-5011	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Karina BLUE PVC COMPOUND 360-06/858-IS-SD (FREE) (***)	Karina Ind. e Com. de Plásticos Ltda	Polyolefin, Unspecified	Karina
CYCOLAC™ EX58 resin	SABIC Innovative Plastics	ABS	CYCOLAC™