Generic Nylon 6I/6T - Glass Fiber
| Category: | Nylon 6I/6T , Polyamide 6I/6T Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R1oxp7_Generic-Nylon-6I-6T---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6I/6T - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.44 to 1.79 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.10 to 0.71 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 3.0 to 3.5 | % | |
| Equilibrium, 23°C, 50% RH | 1.2 to 1.8 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 280 to 361 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 to 23300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 190 to 262 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 to 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 to 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 to 80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 280 to 291 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 140 to 215 | °C | ISO 75-2/C |
| Continuous Use Temperature | 140 to 250 | °C | ASTM D794 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.5E-5 to 2.0E-5 | cm/cm/°C | |
| Transverse | 4.0E-5 to 5.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (23°C) | 30 to 35 | kV/mm | IEC 60243-1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECAPEI™ TECAPEI™ | Ensinger Inc. | PEI | TECAPEI™ |
| Ultramid® B3WG6 GIT BK807 | BASF Corporation | Nylon 6 | Ultramid® |
| KOCETAL® UR302BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| ICORENE® N9702 | ICO Polymers EMEA, A Division of A. Schulman | PUR-Ester | ICORENE® |
| Sylvin 9413-85UV Clear 876 | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |