| UV Stabilized High Viscosity Acetal Homopolymer with Very Low Emissions |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.4 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.9 | % | ISO 294-4 |
| Flow | 2.1 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M scale | 90 | ISO 2039-2 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 40 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 370 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 94.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| Annealing Time - Optional | 30.0 | min/mm | |
| Annealing temperature | 160 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | mg/kg | VDA 275 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 205 | °C | |
| Mold Temperature, Optimum | 90 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 8.00 | s/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extrusion Melt Temperature, Optimum | 200 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (100 Hz) | 3.96 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 2.7E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 200 - 210 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Holding Pressure | 90.0 - 110 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Melt Temperature | 195 - 205 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE5305B | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Supol HP908E | LyondellBasell Industries | PP Copolymer | Supol |
| Vynaprene 7907 | Axiall Corporation | PVC, Rigid | Vynaprene |
| Karina WHITE PVC COMPOUND 650-10/ 1-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF00CSXS compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |