EPO-TEK® CF6-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R0XCRS_EPO-TEK-CF6-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® CF6-2 is a two component, high temperature and high Tg epoxy designed for fiber optic packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 110 | °C | |
| CLTE - Flow | |||
| -- 2 | 6.9E-5 | cm/cm/°C | |
| -- 3 | 1.8E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.534 | ||
| Transmittance (700 to 2000 nm) | > 97.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 360 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 1.98 | GPa | |
| Weight Loss on Heating | |||
| 250°C | 0.13 | % | |
| 300°C | 0.69 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part A | 1.21 | g/cm³ | |
| Part B | 1.22 | g/cm³ | |
| Viscosity 7(23°C) | 0.80 to 1.2 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 1100 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 | ||
| Lap Shear Strength (23°C) | 7.89 | MPa | |
| Relative Permittivity (1 kHz) | 2.99 | ||
| Volume Resistivity (23°C) | > 1.8E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 5.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 920-AP | Anderson Development Company | PUR-Est/eth,TDI | Andur |
| Chemlon® 125 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Delta ATR-2G50 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| LEXAN™ OQ4005 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 700-35/ 1-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |