TOTAL Polystyrene Crystal 1540 (EU)
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qwk8rF_TOTAL-Polystyrene-Crystal-1540-EU-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYSTYRENE CRYSTAL 1540 is an easy flowing crystal polystyrene designed for extrusion or injection applications. In extrusion, it allows to increase extruder output and thermoforming cycle times when mixed with a high impact polystyrene such as POLYSTYRENE IMPACT 7240. Having high gloss, it is particularly suitable for glossy-layer co-extrusion. In injection moulding, POLYSTYRENE CRYSTAL 1540 with this low viscosity at high shear rate has a good injectability and combines an excellent fluidity with a higher softening point. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Melt volume-flow rate (200°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | < 0.10 | % | ISO 62 |
| Saturation | 0.10 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 42.0 | MPa | ISO 527-2 |
| Break | 45.0 | MPa | ISO 527-2 4 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Tensile Creep Modulus (1 hr) | 3000 | MPa | ISO 899-1 5 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | |||
| -- | 8.0 | kJ/m² | ISO 179/1eU |
| 23°C | 14.0 | kJ/m² | ISO 179/1eU 6 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 83.0 | °C | ISO 75-2/A |
| 1.8 MPa | 83.0 | °C | ISO 75-2 7 |
| Vicat Softening Temperature | |||
| -- | 91.0 | °C | ISO 306/A50 |
| -- | 86.0 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 84.0 | °C | ISO 306 8 |
| CLTE | |||
| Flow | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 7.0E-5 | cm/cm/°C | ISO 11359-2 9 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | > 1.0E+15 | ohms | IEC 60093 |
| -- | 1.0E+14 | ohms | IEC 60093 10 |
| Electric Strength | 140 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | ISO 1210 11 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SMOKEGUARD™ III 1096 NATURAL | AlphaGary | PVC, Unspecified | SMOKEGUARD™ III |
| TARFLON™ G1910 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Trilliant™ HC HC7300-0013 ESD Black | PolyOne Corporation | ABS | Trilliant™ HC |
| TRIMMA® SD6390H | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| Durethan® B 40 FA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |