DOW™ HDPE DMDA-8007 HEALTH+™
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QuCryn_DOW-HDPE-DMDA-8007-HEALTH-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow HDPE DMDA-8007 HEALTH+™ is a narrow molecular weight distribution high density homopolymer designed to offer excellent stiffness, low warpage, good toughness, and good moldability. The resin is suitable for injection-molded medical devices such as IV kit components and respiratory care as well as caps and closures for pharmaceutical packaging. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.965 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 8.3 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 180 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 2.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 31.0 | MPa | ASTM D638 |
| Fracture | 17.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 350 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1410 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 83.9 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 133 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 120 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPELIN® FS 340-03 | MOL Petrochemicals Co. Ltd. | MDPE | TIPELIN® |
| TULAMID® PA-IR | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| DINALON® B1X25 HI | Grupo Repol | Nylon 6 | DINALON® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |