LAMIGAMID® 600
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qu8wgg_LAMIGAMID-600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.25 | % | ISO 62 |
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 68.0 | MPa | ISO 527-2 |
| Fracture | 117 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 60 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 20% strain | 103 | MPa | ISO 604 |
| 10% strain | 83.0 | MPa | ISO 604 |
| 5% strain | 50.0 | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.020 - 0.080 | ASTM D1894 | |
| With steel-static | 0.32 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | > 90 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 167 | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.27 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | IEC 60250 | |
| Dissipation Factor | 3.5E-3 | IEC 60250 |
| Additional Information |
|---|
| Creep Rate Stress, DIN 53444, 1% Elongation: 13 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: 22 N/mm²Friction Wear: 0.90 µm/KmCoef of Friction, ASTM D1894, vs. Steel-Dynamic: 0.02 to 0.08Penetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3bSafe Temperature Range, short periods: 140°CSafe Temperature Range, permanent: -40° to 100°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 7050 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| NatureFlex™ 450NPU | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| FireCon™ CPE 30-33 RoHS BLACK | PolyOne Corporation | CPE | FireCon™ |
| Hostacom PPU X9067HS | LyondellBasell Industries | PP Copolymer | Hostacom |
| POLYFLAM® RIPP 3625 CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |