3M™ Dyneon™ Fluoroelastomer FC 2124

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QtOgBy_3MDyneonFluoroelastomerFC2124.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FC 2124 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2124 has an incorporated bisphenol cure system Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Proprietary incorporated cure technology Excellent hot tear properties for moulding articles with complex geometric profiles Process target: injection and transfer moulding, extrusion, bonding and calendering Faster curing version of 3M™ Dyneon™ Fluoroelastomer FC 2123 Clean running with excellent mould release Excellent compression set resistance for moulded goods Typical Applications 3M™ Dyneon™ Fluoroelastomer FC 2124 is suitable for the manufacture of moulded goods and products which require a good bonding between rubber and metal.

Message

3M™ Dyneon™ Fluoroelastomer FC 2124 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2124 has an incorporated bisphenol cure system

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Proprietary incorporated cure technology

Excellent hot tear properties for moulding articles with complex geometric profiles

Process target: injection and transfer moulding, extrusion, bonding and calendering

Faster curing version of 3M™ Dyneon™ Fluoroelastomer FC 2123

Clean running with excellent mould release

Excellent compression set resistance for moulded goods

Typical Applications
3M™ Dyneon™ Fluoroelastomer FC 2124 is suitable for the manufacture of moulded goods and products which require a good bonding between rubber and metal.

General Information
Features	Adhesiveness Good demoulding performance
Uses	Bonding
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	23	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	70		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	3.60	MPa	ASTM D412A
Tensile Strength ²	16.5	MPa	ASTM D412A
Tensile Elongation ³(Break)	300	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	22	%	ASTM D1414
200°C, 70 hr ⁵	20	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
SEETEC EVA VA910	Lotte Chemical Corporation	EVA	SEETEC EVA
Ad-Tech Urethanes LUC-4103	Ad-Tech Plastic Systems Corp.	PUR, Unspecified	Ad-Tech Urethanes
Braskem PP TI4015F	Braskem America Inc.	PP Impact Copolymer	Braskem PP
KOPHOS® KO1365H	Kolon Plastics, Inc.	PC	KOPHOS®
CALIBRE™ MEGARAD™ 2080-15	Trinseo	PC	CALIBRE™ MEGARAD™