Toyolac® 450Y MH5
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QskQFL_Toyolac-450Y-MH5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 450Y MH5 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 450Y MH5 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 55.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 11 | % | ASTM D638 |
| Break | > 10 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 2600 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 86.0 | MPa | ASTM D790 |
| -- 5 | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 120 | J/m | |
| 23°C, 12.7 mm | 98 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 A TF 10 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Telcar® TL-1536D | Teknor Apex Company | TPE | Telcar® |
| Axiall PVC HF-6597 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina GRAY COLOR CONCENTRATE 18/387-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1/CF/20/TF/15/SI/2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |