Zytel® 70G35EF BK538

Category:	Nylon 66 , NYLON RESIN
Manufacturer:	DuPont Performance Polymers
Trademark:	Zytel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QqHbon_Zytel70G35EFBK538.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
35% Glass Reinforced, Heat Stabilized, Polyamide 66

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Additive	heat stabilizer demoulding
Features	Thermal Stability
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Tensile Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>PA66+PA6-GF35
Resin ID (ISO 1043)	PA66+PA6-GF35

Physical	Dry	Conditioned	Unit	Test Method
Density	1.40	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Transverse flow	1.0	--	%	ISO 294-4
Flow	0.40	--	%	ISO 294-4
Water Absorption				ISO 62
Saturated, 23°C, 2.00mm	5.5	--	%	ISO 62
Balance, 23°C, 2.00mm, 50% RH	1.7	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	11000	8500	MPa	ISO 527-2
Tensile Stress (Break)	200	140	MPa	ISO 527-2
Tensile Strain (Break)	2.8	4.6	%	ISO 527-2
Flexural Modulus	9500	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-40°C	9.0	--	kJ/m²	ISO 179/1eA
-30°C	9.0	--	kJ/m²	ISO 179/1eA
23°C	10	--	kJ/m²	ISO 179/1eA
Notched Izod Impact (23°C)	10	--	kJ/m²	ISO 180/1A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	250	--	°C	ISO 75-2/A
8.0 MPa, not annealed	110	--	°C	ISO 75-2/C
Glass Transition Temperature ¹	80.0	20.0	°C	ISO 11357-2
Vicat Softening Temperature	255	--	°C	ISO 306/B50
Melting Temperature ²	260	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow	1.7E-5	--	cm/cm/°C	ISO 11359-2
Lateral	8.5E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	1.0E+14	1.0E+11	ohms·cm	IEC 60093
Dielectric Strength	36	31	kV/mm	IEC 60243-1
Comparative Tracking Index	575	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate ³(1.00 mm)	< 100	--	mm/min	ISO 3795
Flame Rating				UL 94, IEC 60695-11-10, -20
0.70 mm	HB	--		UL 94, IEC 60695-11-10, -20
1.5 mm	HB	--		UL 94, IEC 60695-11-10, -20
Oxygen Index	24	--	%	ISO 4589-2
FMVSS Flammability	B	--		FMVSS 302

Fill Analysis	Dry	Conditioned	Unit
Specific Heat Capacity of Melt	2130	--	J/kg/°C
Thermal Conductivity of Melt	0.24	--	W/m/K

Injection	Dry	Unit
Melt Temperature, Optimum	295	°C
Mold Temperature, Optimum	100	°C
Drying Recommended	yes
Hold Pressure Time	3.00	s/mm
Maximum Screw Tangential Speed	200	mm/sec

Fill Analysis	Dry	Conditioned	Unit
Melt Density	1.24	--	g/cm³
Ejection Temperature	210	--	°C

Injection	Dry	Unit
Drying Temperature	80	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Suggested Max Moisture	0.20	%
Processing (Melt) Temp	285 - 305	°C
Mold Temperature	70 - 120	°C
Holding Pressure	50.0 - 100	MPa

Note Message
1 .	10°C/min
2 .	10°C/min
3 .	FMVSS 302

Resin Grade	Manufacturer	Category	Trademark
NuSil CV1-8151	NuSil Technology	Silicone	NuSil
BCC Resins BC 8635E	BCC Products Inc.	TSU	BCC Resins
DINAPLEN® PPH1S04 G20	Grupo Repol	PP Homopolymer	DINAPLEN®
Geon™ Vinyl Flexible A75M1 Trans 9000	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
ELASTOSIL® R 512/70	Wacker Chemie AG	Silicone	ELASTOSIL® R