TECHNYL® A 30H1 V25 BLACK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qpxkgp_TECHNYL-A-30H1-V25-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame-retardant polyamide 66, 25% glass-fibre reinforced, heat stabilized for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.54 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8800 | 7000 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 95.0 | 78.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.5 | 3.0 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 45 | 47 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 9.8 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.60 mm | 775 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 275 to 280 | °C | |
| Middle Temperature | 280 to 285 | °C | |
| Front Temperature | 285 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT159 (Film Extrusion) | Sasol Polymers | LDPE | Sasol Polymers PE |
| Spartech Polycom SS1070U | Spartech Polycom | ASA | Spartech |
| NEFTEKHIM PP 1365S (H22S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| NEFTEKHIM PP 1532B (YD50G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| KOPLA PA6 KNE1010 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |