KetaSpire® KT-820SFP
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | KetaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QpwFd3_KetaSpire-KT-820SFP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KetaSpire® KT-820SFP is the low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-colored, super-fine powder form. This super-fine PEEK powder is suitable for water-borne coatings, electrostatically driven powder coatings, and resin pre-impregnation of continuous fiber composites. This super-fine powder is produced to a median particle size D50 of about 30 micrometers. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to acids, bases and a broad range of aggressive organic chemicals, best in class fatigue resistance, high thermal resistance, high purity and ease of melt processing. These properties make KT-820SFP well-suited for applications in health care, transportation, electronics, chemical processing and other industrial uses. The resin is also available in a natural-colored pellet form under the grade name KT-820 NT for injection molding and extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Particle Size | |||
| D50 | 30.0 | µm | |
| D90 | 60.0 | µm | |
| D99 | 125 | µm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3650 | MPa | ASTM D638 |
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.2 | % | ASTM D638 |
| Fracture 1 | 20 - 30 | % | ASTM D638 |
| Flexural Modulus | 3860 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 157 | °C | ASTM D648 |
| Glass Transition Temperature | 150 | °C | ASTM D3417 |
| Melting Temperature | 340 | °C | ASTM D3417 |
| CLTE - Flow (-50 to 50°C) | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Injection instructions |
|---|
| Back Pressure: minimum |
| Note Message | |
|---|---|
| 1 . | Tensile test speed = 2 in/min (50 mm/min) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Exceed™ 1518HA | ExxonMobil Chemical | mPE | Exceed™ |
| ECO PELLET® LA17C | UMG ABS, Ltd. | PLA+ABS | ECO PELLET® |
| Keltan® 1500R | LANXESS Buna GmbH | EPDM | Keltan® |
| PENTAMID A GK40 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| SIBUR Synthetic Rubber SBR-1723 Grade B | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |