COSMOPLENE® FL7632L
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QnRaLh_COSMOPLENE-FL7632L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE FL632L is Polypropylene Terpolymer product designed for cast PP with low heat seal temperature, high transparency and roll mark free at high speed. COSMOPLENE FL7632L is suitable for heat sealing layer for dry lamination with BOPP film. FL7632L contains slip and anti-blocking agents. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 44.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 850 | % | ASTM D638 |
| Apparent Bending Modulus | 830 | MPa | ASTM D747 |
| Coefficient of Friction (vs. Itself - Static) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | Internal Method | ||
| MD : 30 µm | 420 | MPa | |
| TD : 30 µm | 440 | MPa | |
| Seal Initiation Temperature (30 µm) | 120 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 132 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm) | 150 | ASTM D2457 | |
| Haze (30.0 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 235 | °C | |
| Take-Off Roll | 26.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1099 X 117578 D | RTP Company | PBT | RTP |
| TIPPLEN® H 483 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| CALP WW567 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| INSTRUC PSUGF10 | Infinity LTL Engineered Compounds | PSU | INSTRUC |
| LNP™ VERTON™ MV006BS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |