Vyncolit® G867 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
Vyncolit G867 is a glass fiber and cellulose filled phenolic molding compound with good mechanical and thermal properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material Fiber filler
Appearance	Black
Forms	Particle
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.77	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.20 - 0.35	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.15	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Injection Molded)	15000	MPa	ISO 527-2
Tensile Stress (Break, Injection Molded)	45.0	MPa	ISO 527-2
Tensile Strain (Break, Injection Molded)	0.55	%	ISO 527-2
Flexural Modulus (Injection Molded)	10000	MPa	ISO 178
Flexural Stress (Injection Molded)	110	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Injection Molded)	3.5	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	7.0	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	180	°C	ISO 75-2/A
8.0 MPa, not annealed	150	°C	ISO 75-2/C
Linear thermal expansion coefficient			ASTM E831
Flow	3.5E-5	cm/cm/°C	ASTM E831
Lateral	4.0E-5	cm/cm/°C	ASTM E831

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	25	kV/mm	IEC 60243-1
Comparative Tracking Index	175	V	IEC 60112

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.60 mm	HB	UL 94
4.00 mm	V-0	UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Injection Pressure	100 - 248	MPa
Holding Pressure	30.0 - 89.6	MPa
Back Pressure	4.83 - 15.2	MPa

Injection instructions
Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.7 to 0.85 g/cm³Post Shrinkage, ISO 2577: 0.1 to 0.2%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 170 to 190°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 140 to 160°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 30 to 40 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 35 to 45 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 100 to 120 MPaFlexural Modulus, ISO 178, Injection Molding: 9 to 11 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.9 to 1%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 35 to 55 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 14 to 16 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.5 to 0.6%Charpy Notched Impact Strength, ISO 179, Injection Molding: 2.5 to 4.5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 6 to 8 kJ/m²Compressive Strength, ISO 604: 130 to 150 MPa

Injection instructions

Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.7 to 0.85 g/cm³Post Shrinkage, ISO 2577: 0.1 to 0.2%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 170 to 190°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 140 to 160°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 30 to 40 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 35 to 45 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 100 to 120 MPaFlexural Modulus, ISO 178, Injection Molding: 9 to 11 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.9 to 1%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 35 to 55 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 14 to 16 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.5 to 0.6%Charpy Notched Impact Strength, ISO 179, Injection Molding: 2.5 to 4.5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 6 to 8 kJ/m²Compressive Strength, ISO 604: 130 to 150 MPa

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QiRUlz_Vyncolit-G867.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
AIE ABS 2010CF	Asia International Enterprise (Hong Kong) Limited	ABS	AIE ABS
Fainplast PVC KL 101	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
LUVOCOM® 1105-8592	Lehmann & Voss & Co.	PEEK	LUVOCOM®
POLYfill PP EIP5025 F VT2	Polykemi AB	PP+EPDM	POLYfill
PENTAMID B L10 H yellow 1021	PENTAC Polymer GmbH	Nylon 6	PENTAMID B